HuaYuan Chemical Industry Co., Ltd.  

HOME  |  CHINESE  |  ENGLISH

 
Site search:
 
home     |     about us     |     products     |     honors     |     news     |     order     |     contact us     |     chinese
 
 
products
Synthetic camphor series
Graphite series
molybdenum chemical series
Ethephon series
Antioxidant series
Silicide series
Phosphorus chloride series
Adhesive series
Nylon series,modified nylon series
Reagent
Solvent, Auxiliary agent
Fine chemical institute
Bulk drink water bottle
products
HOME >> PRODUCTS

Typical properties for grades of"SANLU"brand PA

PA 66 SERIES

Items

 



Test Method

Flexing resistance PA66

Flame retardant PA66

Flame retardant reinforced super toughness PA66

Short glass fiber reinforced PA66

Type

ST-102

FR-102A

FR-302

SG1-25 SG1-30 SG1-35 SG1-40 SG1-45

Characteristic

Contain elastomer.High lmpact& resistance to low temp.

Nitride flame retardant.High strength & low distortion

centain 25%-45% short glass fiber,elastomer & bromide flame retardant.High impact&resislance to low temp.

Contain 25%-45% short glass fiber.High strength & low distortion.

Filler

 

 

 

30

25 30 35 40 45

Flammabitity

UL94

HB

V-0

V-0

HB

Relative Density

GB1033

1.08

1.16

1.38

1.37

Melting Range (°C)

 

255

255

255

255

Tensile Strength (MPa)

GB1040

47

53

150

170

Relative (%) Elongation

 

53

2

4

2

Flexural Strength (MPa}

GB1042

76

100

180

240

Flexural Modulus (MPa)

 

1625

2645

5000

7800

Impact Str.Notched (KJ/m2)

GB1034

116

9

9.5

15

Hot Temp. Distortion 1.81 MPa (°C)

GB1634

60

150

230

220

Volume Resistivify (.m)

GB1410

1013

1013

1012

1013

Dielectric Constant (60MHz)

GB1409

2.9

3.5

3.6

1.7

Dissipation Factor (1MHz)

GB1409

0.01

0.014

0.012

0.01

PA 1010 SERIES

Items

Test Method

Flame relardantPAl010

Short glass fiber reinforced PAl010

Type

FR-10

SG25 SG30 SG35 SG40 SG45

Nltride flame retardant.

Contain 25%-45%short glass fiber, High strength&good dimensional stability.

Characteristic & Application

Filler

 

 

25 30 35 40 45

Flammabitity

UL94

V-0

HB

Viscosity Nuber (ml/g)

 

 

 

Relative Density

GBl033

1.14

1 3............-5

Melting Range (°C)

 

240

240

Tensile Strength (MPa)

GBl040

47

1 20

Relative (%) Elongation

 

35

2

Flexural Strength (MPa}

GBl042

86

160

Flexural Modulu (MPa)

 

2140

6500

Impact Str.Notched (KJ/m2)

GBl043

11

15

Hot Temp. Distortion 1.81 MPa (°C)

GBl634

64

1 85

Volume Resistivify (.m)

GBl410

1013

1012

Dielectric Constant (60MHz)

GBl409

3.0

2.5

Dissipation Factor (1MHz)

G81409

0.01

0.018

PA 6 SERISE

Items

 

Test Method

Mineral filled Pa66

Flame retardant PA6

Flame retardant PA6

Reinforced super toughness PA6

Shod glass fiber reinforced PA6

Type

MR-401

FR-201

FR-301

ST-301

SG11-25 SG11-30 SG11-35 SG11-40 SG11-45

Characteristic

Contain 40% mineral.Low distortion & Medium strength.

Contain elastomer.High impact& resistance to low temp.

Nitride flame retardant.High st rength& low distortion.

Contain 25-45% short glass fiber& elastomer.High impacl& resistance to low temp.

Contain 25-45% short glass fiber.
High strength& low distortion.

Filler

 

40

20

 

30

25 30 35 40 45

Flammabitity

UL94

HB

V-0

V-0

V-0

HB

Relative Density

GB1033

1.38

1.37

1.16

1.36

1.37

Melting Range (°C)

 

 

215

215

215

215

Tensile Strength (MPa)

GB1040

78

116

65

130

150

Relative (%) Elongation

 

6

2

2

2

3

Flexural Strength (MPa}

GB1042

110

163

100

150

200

Flexural Modulus (MPa)

 

4040

6135

2403

4140

6500

Impact Str.Notched (KJ/m2)

GB1034

9

12

9

38

21

Hot Temp.Distortion 1.81 MPa (°C)

GB1634

80

204

83

200

195

Volume Resistivify (.m)

GB1410

1015

4.2-1012

1013

1013

1012

Dielectric Constant (60MHz)

GB1409

2.2

1.8

3.6

 

2.3

Dissipation Factor (1MHz)

GB1409

0.01

0.01

0.016

 

0.023

Remark: Datas for reference only.

 